TITLE:
Computational Analysis of the Metal Free-Surface Instability, Fragmentation, and Ejecta under Shock
AUTHORS:
Jingsong Bai, Tao Wang, Jiaxin Xiao, Bing Wang, Han Chen, Lei Du, Xinzhu Li, Qiang Wu
KEYWORDS:
Interface Instability, Particle Ejecta, High-Speed Collision, Spallation
JOURNAL NAME:
World Journal of Mechanics,
Vol.7 No.9,
September
25,
2017
ABSTRACT: We conducted numerical simulations of the related processes of interface instability, tensile fragmentation, and jetting resulting from four kinds of typical macro defect perturbations (chevron, sine wave, rectangle, and square) on a Cu free surface under a reflected shock wave when Cu impacts a solid wall at a speed of 2.5 km/s and found that, for the chevron and sine wave cases, the ejecta velocities of the head are 6.28 and 5.88 km/s, respectively. Some parts of the inner material are in a tensile state without any fragmentation, which is observed only in the main body of the material owing to the tension effect. Furthermore, for the other two initial perturbations (rectangle and square), the highest ejecta velocities may even reach 9.14 and 9.59 km/s, respectively. Fragmentation caused by multilayer spallation can be observed on a large scale in the Cu main body, and there are granules in the front area of the ejecta but the degree to which fragmentation occurs is much less in the Cu main body and there is a notable high-speed, low-density granule area in the ejecta head. Finally, we present a detailed analysis of the spatial distribution of the granules, ejecta mass, pressure, temperature, and grid convergence.