Article citationsMore>>

Yin, Y., Gan, Z., Sun, Y., et al. (2010) Controlled Synthesis and Photoluminescence Properties of BaXO₄ (X = W, Mo) Hierarchical Nanostructures via a Facile Solution Route. Materials Letters, 64, 789-792.

has been cited by the following article:

• TITLE: Microwave Synthesis and Photoluminescence Properties of BaWO4 of Homogeneous Double Cone Structure

  AUTHORS: Dengfeng Wu, Shihao Luo, Shuibin Yang, Xuehong Liao

  KEYWORDS: Barium Tungstate, Nanomaterial, Microwave Synthesis, Photoluminescence

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.5 No.4, April 30, 2017

  ABSTRACT: Barium tungstate of homogeneous double cone structure was synthesized by microwave synthesis method with sodium tungstate, barium nitrate as raw materials, polyethylene glycol (PEG2000) as surfactant. The as-prepared sample was characterized by X-ray diffraction (XRD), scanning electron micrograph (SEM) and photoluminescence spectrum (PL). The XRD Pattern showed that the samples are scheelite structure of BaWO4. The SEM image showed that the majority of as-prepared sample is a double cone structure, and some particles are attached to it. The length of most of the double cone is 10 μm. PL spectra showed that as-prepared sample had strong luminescence properties, and it had purity green emission at 495 nm and 521 nm. The effects of different surface active agent on the luminescence properties were studied. The results showed that when PEG2000 is as surfactant, the luminescence intensity of as-prepared sample was maximum.