Li, C.L., Zhang, B. and Fu, Z.W. (2006) Physical and Electrochemical Characterization of Amorphous Lithium Lanthanum Titanate Solid Electrolyte Thin-Film Fabricated by E-Beam Evaporation. Thin Solid Films, 515, 1886-1892.
http://dx.doi.org/10.1016/j.tsf.2006.07.026

has been cited by the following article:

• TITLE: Preparation and Characterization of La0.67–x Li3x TiO3 Solid-State Electrolyte Used for Electrochromic Mirrors

  AUTHORS: Le Dinh Trong, Nguyen Nang Dinh, Do Hong Thanh

  KEYWORDS: Ionic Conductivity, Electron Beam Deposition, All-Solid-State Electrochromic Mirror, Impedance Measurement, Reflectance Spectra

  JOURNAL NAME: Materials Sciences and Applications, Vol.7 No.11, November 11, 2016

  ABSTRACT: With the aim of producing all-solid-state electrochromic mirrors, La0.67–xLi3xTiO3 (LLTO) and the WO3 were prepared by electron beam deposition. The LLTO (with x = 0.11) powder was synthesized by thermally ball-grinding method and the Li+ ionic conductivity of the LLTO ceramic targets was found to be of ca. 3.25 × 10–3 S/cm. Using LLTO targets for e-beam evaporation, 300 nm-thick films with the Li+ ionic conductivity of 5.50 × 10–5 S/cm were deposited. Combining LLTO films with WO3/ITO and LiMn2O4 layers, all-solid-state electrochromic mirrors with a laminar structure of Al/LiMn2O4/LLTO/WO3/ITO were prepared. The reversible reflectance of the mirrors was well controlled by applying polarized potentials onto the ITO electrode. The obtained results suggest useful applications for electrochromic windows working as a smart reflectance mirror that can be used for auto rear-view mirrors.