Mitoseriu, L., Ciomaga, C.E., Buscaglia, V., Stoleriu, L., Piazza, D., et al. (2007) Hysteresis and Tunability Characteristics of Ba(Zr,Ti)O3 Ceramics Described by First Order Reversal Curves Diagrams. Journal of the European Ceramic Society, 27, 3723-3726. http://dx.doi.org/10.1016/j.jeurceramsoc.2007.02.085

has been cited by the following article:

• TITLE: Structural Morphological and Dielectric Properties of Pb1-xNixTiO3 Doped with Ni

  AUTHORS: A. Tawfik, O.M. Hemeda, D.M. Hemeda, R. Shady, M. Barakat

  KEYWORDS: Lead Titanate, Co-Precipitation Method, Dielectric Constant, Transmission Electron Microscope

  JOURNAL NAME: Open Journal of Applied Sciences, Vol.6 No.11, October 31, 2016

  ABSTRACT: In this paper, we have reported a conformable PbTiO3 ceramics doped with Ni by standard double sintering technique as well as chemical co-precipitation method which were successfully synthesized by means of carefully controlled processing parameters. Single phase formation was confirmed through X-Ray Diffraction (XRD) analysis, IR spectroscopy, SEM micrograph and TEM images. Discussion and comparison between both preparation methods were made on the basis of observed results. The tetragonality c/a decreased from 1.049 to 1.0276 for ceramic samples and decreased from 1.06519 to 1.0365 for co-precipitation samples by increasing Ni content. TEM images show small ferroelectric domains of about 3 to 14 nm for the co-precipitation sample and 26 to 48 nm for the ceramic samples. The SEM of co- precipitation samples shows that the microstructure is very dense. The behavior of ε identifies that our samples are nonrelaxor. Increasing the Ni concentration increases the value of dielectric constant and the Tc is shifted to lower temperature.