Article citationsMore>>

G. T. Park, S. U. Koh, H. G. Jung and K. Y. Kim, “Effect of Microstructure on the Hydrogen Rapping Efficiency and Hydrogen Induced Cracking of Pipeline Steel,” Corrosion Science, Vol. 50, No. 7, 2008, pp.1865-1871. doi:10.1016/j.corsci.2008.03.007

has been cited by the following article:

• TITLE: Influence of S Contents on the Hydrogen Blistering and Hydrogen Induced Cracking of A350LF2 Steel

  AUTHORS: Shu-qi Zheng, Chang-feng Chen, Li-qiang Chen

  KEYWORDS: A350LF2, S Content, Hydrogen Blistering, Hydrogen Induced Cracking

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.7, July 29, 2011

  ABSTRACT: In the present work, the effects of chemical compositions on the hydrogen blistering and hydrogen induced cracking of A350LF2 steel with different S contents were studied. Four types of A350LF2 steels were evaluated by immersing samples in H2S-saturated NACE solution. The hydrogen blistering, crack length rate(CLR), crack thickness rate(CTR) and crack sensitivity rate(CSR) were evaluated. The results show that there are many hydrogen blisters on the sample surface with S content of 0.021%, a few on the sample surface with S content of 0.019% and 0.012% and no one on the surface with S content of 0.002%. There were 12, 2 and 1 strips of cracks of longer than 0.3 mm on the evaluated cross sections with S content of 0.021%, 0.019% and 0.012%, respectively. There was no any crack in the sample with 0.002% S. The corrosion rate was also evaluated. The S content has no obvious influence on the corrosion rate.