• TITLE: Recycling of Cobalt by Liquid Leaching from Waste 18650-Type Lithium-Ion Batteries

  AUTHORS: Liangmou Yu, Bo Shu, Shiwen Yao

  KEYWORDS: Component, Cobalt, 18650-Type Lithium-Ion Battery, Leaching, Electrodeposition

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.5 No.4, August 25, 2015

  ABSTRACT: In this work, we recover cobalt from waste 18650-type lithiumion batteries by acid leaching. The cathode material is completely dissolved, after leaching waste batteries by using 10 mol/L industrial sulfuric acid at 70℃ for 1 h. The rate of cobalt leaching is nearly 100%. Removal of sodium carbonate, iron, aluminum and other impurities from the leaching solution was well performed by adjusting the pH to 2-3 with stirring vigorously. Finally, under the conditions of 55℃-60℃ of 240 A/m2 current density, electrodeposition current efficiency was 90.01%, the quality of the electrical output achieved cobalt 1A standard electrolytic cobalt, cobalt until greater than 90% yield. The process is easy and suitable for large-scale lithiumion batteries used in the recovery of valuable metals.