Tan, M., Xin, Q., Li, Z. and Zong, B.Y. (2001) Influence of SiC and Al2O3 Particulate Reinforcements and Heat Treatments on Mechanical Properties and Damage Evolution of Al-2618 Metal Matrix Composites. Journal of Materials Science, 36, 2045-2053.
http://dx.doi.org/10.1023/A:1017591117670

has been cited by the following article:

• TITLE: Identification of Optimum Composition and Mechanical Properties of Al-Ni Metal Matrix Composite

  AUTHORS: Manoj Kumar Pal, Simranjeet Singh Sandhu, Rohan Kalia, Arka Ghosh

  KEYWORDS: Metal Matrix Composite, Aluminum (Al), Nickel (Ni), Fabrication, Testing, Composite

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.3 No.4, July 8, 2015

  ABSTRACT: Composites are materials that are made up of two or more chemically dissimilar phases. In this project aluminum was chosen as matrix material because it was inexpensive, light-weight, strong, tough and corrosion resistant. For the main load bearing phase it was hard, corrosion resistant at room temperature and thermally stable. The stir casting method was used because it was cost-effective and easy, and the particulate reinforcement (nickel) was uniformly distributed throughout the matrix phase. Sand moulding was used to cast the specimens. Specimens with 10, 20, 30 and 40 percentage Nickel were tested and the optimal specimen contained 20% Nickel. The Brinell hardness of Al + 20% Ni increased by 14.80%, Rockwell hardness increased by 2.43%, ultimate tensile strength increased by 1.003% and thermal conductivity of Al + 20% Ni decreased by 24.98% with respect to Aluminum.