Su, F.H., Liu, C.S. and Huang, P. (2013) Friction and Wear of Nanocrystalline Co and Co-W Alloy Coatings Produced by Pulse Reverse Electrodeposition. Wear, 300, 114-125.
http://dx.doi.org/10.1016/j.wear.2013.01.120

has been cited by the following article:

• TITLE: Effect of P Addition on the Thermal Stability of Nanocrystalline Ni-Co-Fe-P Coatings

  AUTHORS: Pinqiang Dai, Lvbo Lin

  KEYWORDS: Nanocrystalline, Ni-Co-Fe-P Coatings, Thermal Stability, Activation Energy

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.4 No.11, November 7, 2014

  ABSTRACT: The thermal stability of nanocrystalline Ni-Co-Fe-P coatings with phosphorus content up to 3.38 wt% prepared by pulsed electrodepostion was studied using XRD, TEM and DSC. It is found that multi-component alloying does improve the thermal stability of nanocrystalline coatings due to a “solution drag effect”. For nanocrystalline Ni-40.41%Co-6.16%Fe-1.63%P coating, P-atoms segregate the grain boundaries during annealing which leads to a higher thermal stability. While due to the higher initial P-concentration in Ni-30.1%Co-2.15%Fe-3.38%P, saturation of P and precipitation occurs earlier leading to a slightly lower stability.