Article citationsMore>>

Liu, Q.C., Zi, Z.F., Zhang, M., Pang, A., Dai, J.M. and Sun, Y.P. (2013) Enhanced Microwave Absorption Properties of Carbonyl Iron/Fe3O4 Composites Synthetized by a Simple Hydrothermal Method. Journal of Alloys and Compounds, 561, 65-70.
http://dx.doi.org/10.1016/j.jallcom.2013.02.007

has been cited by the following article:

• TITLE: Structural and Magnetic Properties of Monophasic Maghemite (γ-Fe2O3) Nanocrystalline Powder

  AUTHORS: Juan Adrián Ramos Guivar, Arturo Isaías Martínez, Ana Osorio Anaya, Luis De Los Santos Valladares, Lizbet León Félix, Angel Bustamante Dominguez

  KEYWORDS: Monophasic Nanomaghemite, Rietveld Refinement, TEM, SAED, M-H Loops, ZFC

  JOURNAL NAME: Advances in Nanoparticles, Vol.3 No.3, August 28, 2014

  ABSTRACT: Structural and magnetic studies of monophasic maghemite (γ-Fe2O3) magnetic nanocrystallites (MNCs) synthesized by the co-precipitation chemical route are reported in this paper. For the synthesis, a starting precursor of magnetite (Fe3O4) in basic medium was oxidized at room temperature by adjusting the pH = 3.5 at 80°C in an acidic medium without surfactants. X-ray diffraction (XRD) pattern shows widened peaks indicating nanometric size and Rietveld Refinement confirms only one single-phase assigned to γ-Fe2O3 MNCs. High Resolution Transmission Electron Microscopy (HR-TEM) demonstrates the formation of nanoparticles with diameter around D ≈ 6.8 ± 0.1 nm which is in good agreement with Rietveld Refinement (6.4 ± 1 nm). A selected area electron diffraction pattern was carried out to complement the study of the crystalline structure of the γ-Fe2O3 MNCs. M(H) measurements taken at different temperatures show almost zero coercivity and remanence indicating superparamagnetic domain and high magnetic saturation.