Poinern, G.E.J., Brundavanam, S. and Fawcett, D. (2012) Biomedical Magnesium Alloys: A Review of Material Properties, Surface Modifications and Potential as a Biodegradable Orthopaedic Implant. American Journal of Biomedical Engineering, 2, 218-240. http://dx.doi.org/10.5923/j.ajbe.20120206.02

has been cited by the following article:

• TITLE: Effect of 45S5 Bio-Glass Particles on Physical Properties and Corrosion Resistance of the Mg-5Zn Matrix Composite

  AUTHORS: M. A. F. Zaludin, S. B. Jamaludin, M. S. Idris, N. A. Llah

  KEYWORDS: Powder Metallurgy; Bio-glass; Magnesium; Corrosion; Density; Porosity

  JOURNAL NAME: Open Journal of Metal, Vol.4 No.1, March 27, 2014

  ABSTRACT: The effect of bio-glass (45S5) addition on the physical properties of Mg-5Zn matrix composite has been investigated. Powder metallurgy method was used to fabricate the composite by mixing, compacting and followed by sintering. Mg-5 wt% Zn was reinforced with 5, 10, 15, 20, 25, and 30 wt% of bio-glass (BG). The physical properties such as density and porosity were determined using a pcynometer. Corrosion resistance was studied by immersion test. The results showed that porosity of the sintered sample decreased for the Mg-5 wt% Zn reinforced with 5 wt% of bio-glass. However, above 5 wt% of bio-glass, the porosity increased. The result also showed that corrosion resistance of Mg-5 wt% Zn increased as the amount of bio-glass increased.