S. F. Chen, J. P. Li, K. Qian, W. P. Xu, Y. Lu, W. X. Huang and S. H. Yu, “Large Scale Photochemical Synthesis of M@TiO₂ Nanocomposites (M = Ag, Pd, Au, Pt) and Their Optical Properties, CO Oxidation Performance, and Antibacterial Effect,” Nano Research, Vol. 3, No. 4, 2010, pp. 244-255. www.springerlink.com

has been cited by the following article:

• TITLE: Electrical Properties of Nano-TiO2 Thin Film Using Spin Coating Method

  AUTHORS: Ayodele Abeeb Daniyan, Lasisi Ejibunu Umoru, Adeniyi Yisau Fasasi, Joseph Olatunde Borode, Kunle Michael Oluwasegun, Samuel Oloruntoba Olugbenga Olusunle

  KEYWORDS: Titanium Oxide; ITO; Spin Coating; KFPPT; Sheet Resistance and Conductivity

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.2 No.1, January 10, 2014

  ABSTRACT: This work investigated the electrical properties of TiO2 thin film on empty glass and ITO glass by spin coating method. Highly transparent titanium oxide thin films were prepared on empty glass and Indium Tin Oxide (ITO) from a titanium (III) chloride precursor. The sheet resistance of the film prepared from both the synthesised and the commercially available TiO2 was measured by the Keithley four-point probe tester (KFPPT). A comparable sheet resistance of 10.69E + 00 Ω/sq was obtained on the ITO. The electrical conductivity of the TiO2 film on ITO glass substrate was found to be very high (3.46E + 05 Ω-1?cm-1) and comparable to that of the bare ITO glass.