H. Schmidt, M. Akarsu, T. S. Müller, K. Moh, G. Sch?fer, D. J. Strauss and M. Naumann, “The Formation of Gradients in Wet Deposited Coatings with Photocatalytically Active Nanoparticles,” Research on Chemical Intermediates, Vol. 31, No. 4-6, 2005, pp. 535-553. doi:10.1163/1568567053956680

has been cited by the following article:

• TITLE: Low Temperature Gas Sensing Coatings Made Through Wet Chemical Deposition of Niobium Doped Titanium Oxide Colloid

  AUTHORS: Naji Al Dahoudi

  KEYWORDS: Colloid, Titanium Oxide, Niobium, Gas Sensor, Spin Coating

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.4, March 22, 2011

  ABSTRACT: Niobium doped titanium oxide (TiO2) colloid was synthesized to fabricate a hydrogen gas sensor layer on oxidized silicon wafer substrate. The layers were obtained using spin coating technique and then heated in air at 500°C for 30 min. The doping of TiO2 led to a significant enhancement of the sensitivity of the layer especially at low operating temperature. The effect of doping was found effective of operating the sensor at relatively low temperature (150°C). The layers show a very smooth nanostructure with average roughness of less than 0.5 nm. The behavior of the sensing characteristics of such layers was discussed related to their chemical compositions, morphology and their crystalline structure. The morphological and structural characteristics of the layers were studied through X-ray diffraction (XRD) and Atomic force microscopy (AFM).