O. S. Chana, R. Kuzhakhmetov, D. M. C. Hyland, J. Eastell, D. Dew-Hughes, C. R. M. Grovenor, Y. Koval, M. Mossle, R. Kleiner, P. Muller and P. A. Warburton, “Fabrication and Measurement of Intrinsic Josephson Junctions in Misaligned Films of Tl2Ba2CaCu2O8,” IEEE Transactions on Applied Superconductivity, Vol. 11, No. 1, 2001, pp. 2711-2714.
http://dx.doi.org/10.1109/77.919622

has been cited by the following article:

• TITLE: Phase Transition in Superconducting Thin Films of Tl System Employing a One-Zone Furnace and Deposited by Spray Pyrolysis

  AUTHORS: Jorge Luis Rosas-Mendoza, L. Perez-Arrieta, Miguel Aguilar-Frutis, Ciro Falcony, R. Vázquez-Arreguín, Alejandro Miguel Rosas-Mendoza

  KEYWORDS: Superconductors; Thin Films; Ultrasonic Spray Pyrolysis

  JOURNAL NAME: Materials Sciences and Applications, Vol.4 No.11, November 26, 2013

  ABSTRACT: A study of the phase transitions in superconducting thin films of the Thallium-Barium-Calcium-Copper (TBCCO) system is carried out. In particular, it was got the Tl-1223 phase. For this purpose, and using the ultrasonic spray pyrolysis technique, Barium-Calcium-Copper precursor films were first obtained. Upon deposition of the precursor films, and as a second step, they were thallium (Tl) diffused in the one-zone furnace at 860°C. This methodology resulted in superconducting films that showed a phase transition as follows: Tl-2223 → Tl-2223 + Tl-2212 → Tl-2212 → Tl-1223, achieved between 2 and 7 hours of thallium diffusion. The evidence of the phase transitions was corroborated by the experimental results of X-ray diffraction, energy dispersive spectroscopy and resistance-temperature measurements.